Solidification and solid-state transformation mechanisms in Si alloyed high-chromium white cast irons.

Public Domain


Details

  • Personal Author:
  • Description:
    Chromium white cast irons are widely used in environments where severe abrasion resistance is a dominant requirement. To improve the wear resistance of these commercially important irons, the United States Bureau of Mines and CSIRO Australia are studying their solidification and solid-state transformation kinetics. A ternary Fe-Cr-C iron with 17.8 wt pct (pct) Cr and 3.0 pct C was compared with commercially available irons of similar Cr and C contents with Si contents between 1.6 and 2.2 pct. The irons were solidified and cooled at rates of 0.03 and 0.17 K · s-1 to 873 K. Differential thermal analysis (DTA) showed that Si depresses the eutectic reaction temperature and suggests that is has no effect upon the volume of eutectic carbides formed during solidification. Microprobe analysis revealed that austenite dendrites within the Si alloyed irons cooled at 0.03 and 0.17 K·s-1 had C and Cr contents that were lower than those of dendrites within the ternary alloy cooled at the same cooling rate and a Si alloyed iron that was water quenched from the eutectic temperature. These lower values were shown by image analysis to be the result of both solid-state growth (coarsening) of the eutectic carbides and some secondary carbide formation. Hardness measurements in the as-cast condition and after soaking in liquid nitrogen suggest an increase in the martensite start temperature as the Si content was increased. It is concluded that Si's effect on increasing the size and volume fraction of eutectic carbides and increasing the matrix hardness should lead to improved wear resistance over regular high-chromium white cast irons. [Description provided by NIOSH]
  • Subjects:
  • Series:
    Mining Publications
  • ISSN:
    0360-2133
  • Document Type:
    Text
  • Genre:
    Journal Article
  • Place as Subject:
  • CIO:
    National Institute for Occupational Safety and Health (NIOSH)
  • Division:
    ALRC - Albany Research Center
  • Topic:
    Workplace Safety & Health
  • Location:
    North America
  • Issue:
    4
  • NIOSHTIC Number:
    nn:10012104
  • Citation:
    Metall Trans, A, Phys Metall Mater Sci 1993 Apr; 24A(4):981-988
  • Federal Fiscal Year:
    1993
  • Peer Reviewed:
    False
  • Source Full Name:
    Metallurgical Transactions. A. Physical Metallurgy and Materials Science
  • Collection(s):
  • Main Document Checksum:
    urn:sha-512:7dc847c09aedf140bc731323e8446b4703641ae07d6ad9e7b7238120dab30b8f7dcaa9b938d34d035f87873a0fe7fec262d5d13dcaf290925445e82b6de3b57d
  • Download URL:
  • File Type:
    Filetype[PDF - 168.02 KB ]
PREVIOUS
ON THIS PAGE
Details
CDC STACKS serves as an archival repository of CDC-published products including scientific findings, journal articles, guidelines, recommendations, or other public health information authored or co-authored by CDC or funded partners.

As a repository, CDC STACKS retains documents in their original published format to ensure public access to scientific information.
BACK TO TOP