Advanced Search
Select up to three search categories and corresponding keywords using the fields to the right. Refer to the Help section for more detailed instructions.

Search our Collections & Repository

All these words:

For very narrow results

This exact word or phrase:

When looking for a specific result

Any of these words:

Best used for discovery & interchangable words

None of these words:

Recommended to be used in conjunction with other fields

Language:

Dates

Publication Date Range:

to

Document Data

Title:

Document Type:

Library

Collection:

Series:

People

Author:

Help
Clear All

Query Builder

Query box

Help
Clear All

For additional assistance using the Custom Query please check out our Help Page

Filetype[PDF-6.21 MB]


Select the Download button to view the document
This document is over 5mb in size and cannot be previewed
  • English
    • Details You May Also Like

    Details:

    • Personal Author:
      Larson, D. E. (Darrell E.)
    • Corporate Authors:
      United States. Bureau of Mines.
    • Description:
      "The U.S. Bureau of Mines investigated fe-base alloys containing 8 pct cr with ni, al, and si additions as substitutes for standard aisi type 304 stainless steel (ss) in high-temperature oxidizing applications. The objective of this study was to reduce the amount of cr required to make an austenitic stainless steel while retaining satisfactory workability, mechanical properties, and oxidation resistance. Alloys prepared in this investigation had a composition of fe-8cr-1mn-0.07C with varying amounts of ni, al, and si. A minimum of 10 pct ni was required to achieve an austenitic composition. The microstructures of the austenitic alloys were very susceptible to room-temperature deformation-induced martensitic transformations. When the alloys were cold-worked or stressed, the materials had far greater tensile strengths than type 304 ss at room temperature. At higher temperatures, tensile strengths and workability of several of the alloys were comparable to that of type 304 ss. Although martensitic transformation caused the room- temperature properties of the experimental alloys to be quite different than those of type 304 ss, the superior oxidation reistance and similar hot workability of several alloys encourage their use as replacements for type 304 ss." - NIOSHTIC-2

      NIOSHTIC no. 10007260

    • Subjects:
    • Series:
      Report of investigations (United States. Bureau of Mines) ; 9255
    • Document Type:
      Report
    • Collection(s):
    • Main Document Checksum:
    • Download URL:
    • File Type:

    Supporting Files

    • No Additional Files

    More +

    You May Also Like

    Checkout today's featured content at stacks.cdc.gov